Do you really understand the difference between rare earth magnet and ferrite magnet?

Magnets are objects that produce magnetic fields that enable them to attract certain metals from afar without touching them. Some magnets are produced naturally and some are man-made. Although there are many different types of magnets, the two most popular artificial magnets are ferrite magnets and rare earth neodymium magnets. Let me talk about some differences between them today.
 
Introduction of the advantages and disadvantages of the two
Rare earth magnets and ferrite magnets are all types of permanent magnets. They are all made of a material that, once charged, will remain magnetic for many years unless damaged. However, not all permanent magnets are the same. Rare earth and ferrite magnets have different strength and resilience because they are made of different metal alloys.
 
ferrite magnet
For many years, all magnets have been natural magnets, such as lodestone, which is a kind of iron ore with magnetic properties. In 1952, magnets were first made of ferrite. By making magnets from ferrites, engineers can make magnets in any shape they want. By making the carefully manufactured mixture into ferrite magnets, a stronger magnetic field can be produced than in nature. Ferrite magnets are cheaper, stronger and soon become popular. Ferrite magnets are also known as hard ferrite magnets or ferromagnets. They are made of strontium or barium ferrite.
 
Rare Earth magnet
There are two types of rare earth magnets: SmCo and NdFeB. SmCo and NdFeB magnets are called "rare earth" because they are made up of rare earth elements (lanthanides) in the periodic table of elements. SmCo magnets were developed in the 1970s and were the first rare earth magnets produced. Nd-Fe-B magnets were listed in 1984.
 
Relative Strength of Ferrite and Rare Earth Magnets
The magnetic field intensity produced by the magnet is quantified by BHmax or maximum energy product, and the BHmax or maximum energy product is measured by MGOe. The higher the BHmax, the greater the force of the magnet. BHmax of ferrite magnet is 3.5, BHmax of SmCo is 26, NdFeB is the most powerful rare earth magnet, BHmax is 40.
 
Relative Resistance of Ferrite to Thermal Stress of Rare Earth Magnets
Magnets begin to lose strength when heated to a certain temperature (Tmax), so they should not operate outside that temperature. However, when cooled below Tmax, they will regain power. The Tmax of ferrite magnet is 300 degrees Celsius, that of SmCo magnet is 300 degrees Celsius, and that of NdFeB magnet is 150 degrees Celsius. If the magnet is heated at a temperature far higher than Tmax, it will eventually be demagnetized at a temperature known as Tcurie. When the magnet is heated to a place other than Tecury, it cannot be restored once it is cooled. Ferrite magnets have a t-Curie value of 460 degrees Celsius, SmCo 750 degrees Celsius and NdFeB 310 degrees Celsius.
 
Relative Durability of Ferrite and Rare Earth Magnets
Magnets can resist not only thermal stress, but also other stresses. Nd-Fe-B magnets are fragile and difficult to process. They are also easy to corrode. SmCo magnets are slightly less brittle and difficult to process, but have high corrosion resistance. SmCo magnets are also the most expensive type of magnet. Ferrite magnets are cheaper than SmCo and NdFeB magnets, and have good demagnetization and corrosion resistance.
 
Every Benefit
Ferrite and neodymium magnet have different advantages. Ferrite magnets are easy to magnetize. They are very corrosion resistant and generally do not require additional coatings for corrosion protection. They can resist the demagnetization of external magnetic fields. They are stronger than natural magnets, although many other types of magnets are stronger than them. They are relatively cheap. Neodymium magnets are the most powerful of all permanent magnets. A neodymium magnet can lift more than any other type of magnet of the same size. They are extremely resistant to demagnetization of external magnetic fields.
 
Every shortcoming
Ferrites and neodymium magnets also have different disadvantages. Ferrite magnets are very fragile and fragile. They can't be used in machinery that is under great pressure or bending. If exposed to high temperatures (over 480 degrees Fahrenheit), they will be degaussed. They only have medium intensity magnetic field, which is not suitable for applications requiring strong magnetic field. Neodymium magnets are relatively more expensive than ferrite magnets. They are easy to rust and extra measures must be taken to protect them from corrosion. Neodymium magnets are also very fragile and break under pressure. If exposed to more than 175 to 480 degrees Fahrenheit (depending on the alloy used), they lose their magnetism.
 
The above is about the difference between rare earth magnet and ferrite magnet. It was edited by Courage Network Department of China Magnet Supplier.

Relevant articles on rare earth magnets;
What is a rare earth magnet? What kinds of rare earth magnets are there?

CONTACT US

Contact: Emily Feng

Phone: 135-5660-1560

Tel: 0769-23388351/2

Email: salesd@dgcourage.com

Add: No. 302, No. 1, Longtong Road, Xinhe Community, Wanjiang District, Dongguan City, Guangdong Province, China